| TPEE G5544 美國杜邦公司 物性數(shù)據 |
| 暫無此原料描述部分┄ |
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據 | 數(shù)據單位 | |||||||||
| 基本性能 | 24小時吸水率 | --- | ASTM D-570 | 1.5 | % | ||||||||
| 物理性能 | 泰伯磨耗量 | CS-17輪 | ASTM D-1044 | 9 | mg/1000rev | ||||||||
| 比重 | --- | ASTM D-792 | 1.22 | --- | |||||||||
| 熔體流動速率 | --- | ASTM D-1238 | 10 | g/10min | |||||||||
| 泰伯磨耗量 | H 18輪 | ASTM D-1044 | 116 | mg/1000rev | |||||||||
| 機械性能 | 硬度計硬度 | --- | ASTM D-2240 | 55 | --- | ||||||||
| 揉曲模量 | 23℃ | ASTM D-790 | 193 | MPa | |||||||||
| 斷裂拉伸力 | --- | ASTM D-638 | 31 | MPa | |||||||||
| 斷裂伸長 | --- | ASTM D-648 | 375 | % | |||||||||
|
--- |
|
|
|
|||||||||
| 埃佐沖擊強度 | 23℃ | ASTM D-256 | 不破裂 | J/m | |||||||||
| 初耐撕裂性能 | --- | ASTM D-1004 | 123 | kn/m | |||||||||
| 熱 性 能 | 熔點 | --- | ASTM D-3418 | 215 | ℃ | ||||||||
| 維卡軟化點 | --- | ASTM D-1525 | 196 | ℃ | |||||||||
| 熱畸變溫度 | @0.5Mpa | ASTM D-648 | 111 | ℃ | |||||||||
| 熱畸變溫度 | @0.18Mpa | ASTM D-648 | 51 | ℃ | |||||||||
| 其它性能 | 耐揉曲切口增長性能 | --- | ASTM D-1052 | >8×105 | |||||||||