| PMMA TPE-30 法國(guó)阿托菲納公司 物性數(shù)據(jù) |
| 暫無(wú)此原料描述部分┄ |
| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 基本性能 | 熔體流動(dòng)速率 | --- | ASTM D-1238 | 14.5 | g/10min |
| 吸水率 | 浸水24hrs后增重 | ASTM D-570 | 0.3 | % | |
| 物理性能 | 成形收縮率 | (冷模/冷件),48hrs | ASTM D-935 | 0.2-0.6 | % |
| 透光率 | --- | ASTM D-1003 | 92 | % | |
| 折射率ND | --- | ASTM D-542 | 1.49 | --- | |
| 比重 | --- | ASTM D-792 | 1.18 | --- | |
| 霧度 | --- | --- | <2 | % | |
| 機(jī)械性能 | 洛氏硬度 | --- | ASTM D-758 | 89 | M scale |
| 拉伸強(qiáng)度 | 初級(jí)應(yīng)變速率0.1cm/cm/min | ASTM D-638 | 670(66) | kgf/cm2(MPa) | |
| 彎曲強(qiáng)度 | 橫跨比=16 | ASTM D-790 | 980(97) | kgf/cm2(MPa) | |
| 彎曲模數(shù) | --- | ASTM D-790 | 31000 | kgf/cm2 | |
| 沖擊強(qiáng)度 | Izod研磨缺口 | ASTM D-256 | 1.2(12.3) | kgf.cm/cm(J/m) | |
| 沖擊強(qiáng)度 | 落錘(15.2×15.2×0.3cm重1.4kg半徑0.64cm) | ASTM D-256 | 14(1.4) | kg.cm(J) | |
| 熱 性 能 | 熱變形溫度負(fù)荷，退火 | 2℃/min,18.6kgf/cm2 | ASTM D-648 | 77 | ℃ |
| 維卡軟化點(diǎn) | 未退火,50℃/hr,1kg | ASTM D-1525 | 88 | ℃ | |
| 維卡軟化點(diǎn) | 未退火,50℃/hr,5kg | ASTM D-1525 | 82 | ℃ | |
| 玻璃化轉(zhuǎn)變溫度Tg | --- | --- | 92 | ℃ | |
| 使用溫度范圍 | 與殘余應(yīng)力大小有關(guān) | --- | 63-77 | ℃ | |