牌號
Trade Mark |
主要成份(%)
Chemical Composition |
特性和用途
Characteristics & Application |
相當AWS
Equivalent to AWS |
|
S201
|
Sn1 Si0.3 Mn0.3
Cu Rem |
機械性能好，抗裂性能好。紫銅氣焊及氬弧焊用。
to gas weld or argon arc weld red copper, and to get good mechanical properties and cracking resistance |
ERCu
|
|
S211
|
Si3 Mn1 Cu Rem
|
機械性能好。銅合金氬弧焊及鋼的MIG釬焊用。
to gas weld copper alloy or to MIG weld steel, and to get good mechanical properties |
ERCuSi-A
|
|
S212
|
Sn5 P0.2 Cu Rem
|
耐磨性好。銅合金氬弧焊及鋼的堆焊用。
to argon arc weld copper alloy or to resurface steel, and to get good resistance to wear |
ERCuSn-A
|
|
S213
|
Sn8 P0.2 Cu Rem
|
耐磨性好。銅合金氬弧焊及鋼的堆焊用。
to argon arc weld copper alloy or to resurface steel, and to get good resistance to wear |
ERCuSn-C
|
|
S214
|
Al7.5 Cu Rem
|
耐磨、耐蝕。銅合金氬弧焊及鋼的堆焊用。
to argon arc weld copper alloy or to resurface steel, and to get good resistance to wear and corrosion |
ERCuAl-A1
|
|
S215
|
Al9 Cu Rem
|
耐磨、耐蝕。銅合金氬弧焊及鋼的堆焊用。
to argon arc weld copper alloy or to resurface steel, and to get good resistance to wear and corrosion |
ERCuAl-A2
|
|
S221
|
Cu60 Sn1 Si0.3
Zn Rem |
熔點約890℃。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵。
melt at about 890℃ to gas weld or carbon arc weld bronze copper, and to braze weld copper, steel or cast iron as well |
|
|
S221F
|
Cu60 Sn1 Si0.3
Zn Rem |
外涂焊劑的S221焊絲。
S221 welding rod coated with flux |
|
|
S222
|
Cu58 Sn0.9 Si0.1
Fe0.8 Zn Rem |
熔點約890℃。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵。
melt at about 890℃ to gas weld or carbon arc weld bronze copper, and to braze weld copper, steel or cast iron as well |
RBCuZn-C
|
|
S222F
|
Cu58 Sn0.9 Si0.1
Fe0.8 Zn Rem |
外涂焊劑的S222焊絲。
S222 welding rod coated with flux |
RBCuZn-C
|
|
S223
|
Cu59 Sn0.6 Zn Rem
|
熔點約900℃。銅、鋼、鑄鐵釬焊用。
melt at about 900℃ to braze weld copper, steel or cast iro |
RBCuZn-A
|
|
S224
|
Cu62 Si0.5 Zn Rem
|
熔點約905℃。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵。
melt at about 905℃ to gas weld or carbon arc weld bronze copper, and to braze weld copper, steel or cast iron as well |
|
|
S225
|
Cu48 Ni10 Zn Rem
|
熔點約935℃。高強度，釬焊鋼、鎳及硬質(zhì)合金用。
melt at about 935℃ to braze weld steel, nickel or kentanium, and to get high strength |
RBCuZn-D
|
|
S225F
|
Cu48 Ni10 Zn Rem
|
外涂焊劑的S225焊絲。
S225 welding rod coated with flux |
RBCuZn-D
|
|
S226
|
Cu60 Sn0.3 Si0.2
Zn Rem |
熔點約900℃。黃銅氣焊用，也可釬焊銅、鋼、鑄鐵。
melt at about 900℃ to gas weld bronze copper, and to braze weld copper, steel or cast iron as well |
|
|
S227
|
Cu58 Sn0.9 Ni0.5
Si0.1 Fe0.8 Zn Rem |
熔點約880℃。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵。
melt at about 880℃ to gas weld or carbon arc weld bronze copper, and to braze weld copper, steel or cast iron as well |
RBCuZn-B
|
|
S229
|
Cu55 Ni6 Mn4
Zn Rem |
熔點約920℃。高強度，釬焊鋼、鎳及硬質(zhì)合金用。
melt at about 920℃ to braze weld steel, nickel or kentanium, and to get high strength |
|
牌號
Trade Mark |
主要成份(%)
Chemical Composition |
特性和用途
Characteristics & Application |
相當AWS
Equivalent to AWS |
|
S301
|
SAl 1070
|
塑性好、耐蝕。純鋁氣焊、氬弧焊用。
to gas weld or argon arc weld aluminum, and to get good ductility and resistance to corrosion |
ER1070
|
|
ER4043
|
SAl 4043
(S311) |
抗裂性好、通用性大。鋁合金氣焊、氬弧焊用。不宜用于鋁鎂合金。
with a wide range of usage to gas weld or argon arc weld aluminum alloy except magaluma, and to get good cracking resistance |
ER4043
|
|
ER5183
|
SAl 5183
|
耐蝕、強度高。鋁合金氬弧焊用。
to argon arc weld aluminum alloy, and to get resistance to corrosion and high strength |
ER5183
|
|
ER5356
|
SAl 5356
|
耐蝕、強度高，通用性大。鋁合金氬弧焊用。
with a wide range of usage to argon arc weld aluminum alloy, and to get resistance to corrosion and high strength |
ER5356
|
|
ER5556
|
SAl 5556
(S331) |
耐蝕、強度高。鋁合金氬弧焊用。
to argon arc weld aluminum alloy, and to get resistance to corrosion and high strength |
ER5566
|
|
牌號
Trade Mark |
主要成份(%)
Chemical Composition |
特性和用途
Characteristics & Application |
相當AWS
Equivalent to AWS |
|
|
S111
|
C1 Cr29 W5
Co Rem |
HRc=40~45，高溫下耐磨、耐蝕。堆焊高溫高壓閥門。
apply to resurface and to get resistance to wear and corrosion at high temperature |
RCoCr-A
|
|
|
S112
|
C1.5 Cr29 W8
Co Rem |
HRc=45~50，高溫下耐磨、耐蝕。堆焊閥門、熱軋孔型。
apply to resurface and to get resistance to wear and corrosion at high temperature |
RCoCr-B
|
|
|
S114
|
C2.5 Cr30 W12
Co Rem |
HRc52，高溫下耐磨、耐熱，但抗沖擊性較差。堆焊牙輪鉆頭。
apply to resurface and to get resistance to wear and corrosion at high temperature, but poor in shock resistance |
RCoCr-C
|
|
|
S190
|
C3.2 Cr27 W14
Co Rem |
HRc55，高溫下耐磨、耐熱，但抗沖擊性較差。堆焊牙輪鉆頭。
apply to resurface and to get resistance to wear and corrosion at high temperature, but poor in shock resistance |
RCoCr-G
|