①原料描述部分 | ||||||
| 規(guī)格級別 | 其它其它注塑 | |||||
| 該料用途 | 超薄壁型電器、電子元件。 | |||||
| ②原料技術(shù)數(shù)據(jù) | ||||||
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
| 基本性能 | 吸水率 | 24hr，in 23℃ | ASTM D-570 | 0.2 | % | |
| 物理性能 | 阻燃性 | 厚度1.47mm (厚度3.05mm ) | UL 94 | 94V-2 | ||
| 透光率 | 厚度3mm | ASTM D-1003 | 88 | % | ||
| 比重 | ASTM D-792 | 1.2 | ||||
| 機械性能 | 彎曲模量 | ASTM D-790 | 2280(23300) | Mpa(kgf/cm2) | ||
| 耐沖擊強度值 | 艾氏、帶缺口厚度3.2mm | ASTM D-256 | 780(80) | j/m(kgfNaN/cm) | ||
| 拉伸強度 | 屈服點 | - | ASTM D-638 | 63(640) | Mpa(kgf/cm2) | |
| 斷裂點 | - | ASTM D-638 | 74(750) | Mpa(kgf/cm2) | ||
| 彎曲強度 | ASTM D-790 | 90(920) | Mpa(kgf/cm2) | |||
| 拉伸模量 | ASTM D-638 | 2170(22100) | Mpa(kgf/cm2) | |||
| 耐沖擊強度值 | 艾氏、帶缺口厚度6.4mm | ASTM D-256 | 100(10) | j/m(kgfNaN/cm) | ||
| 洛氏硬度 | ASTM D-785 | 77 | M標度 | |||
| 壓縮強度 | ASTM D-695 | 77(790) | Mpa(kgf/cm2) | |||
| 拉伸率 | 屈服點 | - | ASTM D-638 | 6 | - | |
| 斷裂點 | - | ASTM D-638 | 140 | - | ||
| 折射率 | ASTM D-542 | 1.585 | ||||
| 電氣性能 | 耐導電徑跡性 | CTI | IEC 112 | 300 | V | |
| 體積電阻率 | ASTM D-257 | 3 | 1016ΩNaN | |||
| 絕緣破壞強度 | 快速加壓值厚度1.6mm | ASTM D-149 | 30 | KV/mm | ||
| 介電率 | 60Hz(106Hz) | ASTM D-150 | 2.95(2.9) | |||
| 介電正切 | 60Hz(106Hz) | ASTM D-150 | 0.0004(0.009) | |||
| 耐電弧性 | ASTM D-495 | 110 | sec | |||
| 加工性能 | 成型收縮率 | 流動方向(垂直方向) | ASTM D-955 | 0.5～0.7 | % | |
| 熱性能 | 負荷撓曲溫度 | 負荷0.451MPa(4.6kgf/cm) | ASTM D-648 | 141 | ℃ | |
| 溫度指數(shù) | 電學式 | 厚度1.47mm | UL 746B | 125 | °C | |
| 沖擊式 | 厚度1.47mm | UL 746B | 115 | °C | ||
| 非沖擊式 | 厚度1.47mm | UL 746B | 125 | °C | ||
| 負荷撓曲溫度 | 負荷1.813MPa(18.6kgf/cm) | ASTM D-648 | 131 | ℃ | ||
| 線膨脹系數(shù) | 流動方向(垂直方向) | ASTM D-696 | 7 | 10-5cm/cm/℃ | ||