產(chǎn)品關(guān)鍵詞：
LCP液晶聚酯,美國杜邦,5130L,
原料技術(shù)數(shù)據(jù) | 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 |
| 基本性能 | 密度 | --- | ISO 1183 | 1620 | Kg/m3 |
| 機械性能 | 斷裂應(yīng)力 | 1.0mm,23℃(73oF) | ISO 527-1,2 | 180 | MPa |
| 斷裂應(yīng)力 | 2.0mm,23℃(73oF) | ISO 527-1,2 | 150 | MPa |
| 斷裂應(yīng)力 | 4.0mm,23℃(73oF) | ISO 527-1,2 | 130 | MPa |
| 斷裂應(yīng)變 | 1.0mm,23℃(73oF) | ISO 527-1,2 | 1.9 | % |
| 斷裂應(yīng)變 | 2.0mm,23℃(73oF) | ISO 527-1,2 | 2.2 | % |
| 斷裂應(yīng)變 | 4.0mm,23℃(73oF) | ISO 527-1,2 | 1.8 | % |
| 拉伸模量 | 1.0mm,23℃(73oF) | ISO 527-1,2 | 16700 | MPa |
| 拉伸模量 | 2.0mm,23℃(73oF) | ISO 527-1,2 | 15300 | MPa |
| 拉伸模量 | 4.0mm,23℃(73oF) | ISO 527-1,2 | 13000 | MPa |
| 彎曲模量 | 1.0mm,23℃(73oF) | ISO 178 | 16200 | MPa |
| 彎曲模量 | 2.0mm,23℃(73oF) | ISO 178 | 12500 | MPa |
| 彎曲模量 | 4.0mm,23℃(73oF) | ISO 178 | 12000 | MPa |
| 彎曲強度 | 1.0mm,23℃(73oF) | ISO 178 | 211 | MPa |
| 彎曲強度 | 2.0mm,23℃(73oF) | ISO 178 | 191 | MPa |
| 彎曲強度 | 4.0mm,23℃(73oF) | ISO 178 | 167 | MPa |
| IZOD沖擊強度 | 3.2mm(0.126in) | ASTM D-256 | 120 | J/m |
| Charpy缺口沖擊強度 | 23℃(73oF) | ISO 179-LeA | 35 | KJ/m2 |
| Charpy無缺口沖擊強度 | 23℃(73oF) | ISO 179-LeU | 35 | KJ/m2 |
| 撓曲溫度 | 1.80MPa | ISO 75-1,2 | 265 | ℃ |
| 介電強度 | 23℃(73?H) | ASTM D-149 | 40 | Kv/mm |
| 電氣性能 | 體積電阻率 | --- | IEC 60093 | >1×1014 | Ohm-cm |
| 表面電阻率 | --- | IEC 60093 | >1×1015 | Ohm |
| 介質(zhì)常數(shù) | 1×102Hz | IEC 60250 | 4.5 | Ohm |
| 介電強度 | 23℃(73?H) | ASTM D-149 | 35 | Kv/mm |
| 介電強度 | 23℃(73?H) | ASTM D-149 | 29 | Kv/mm |
| 介電強度 | 0.8mm(0.032in) | ASTM D-149 | 30 | Kv/mm |
| 介電強度 | 1.6mm(0.063in) | ASTM D-149 | 29 | Kv/mm |
| 介電強度 | 3.2mm(0.126in) | ASTM D-149 | 26 | Kv/mm |
| 介電常數(shù) | 0.8mm(0.032in),23℃(73?H) | ASTM D-150 | 4 | --- |
| 介電常數(shù) | 3.2mm(0.125in),23℃(73?H) | ASTM D-150 | 4.4 | --- |
| 介電常數(shù) | 0.8mm(0.032in),23℃(73?H) | ASTM D-150 | 3.6 | --- |
| 損耗因數(shù) | 3.2mm(0.125in),23℃(73?H) | ASTM D-150 | 0.027 | --- |
| 損耗因數(shù) | 0.8mm(0.032in),23℃(73?H) | ASTM D-2520 B | 0.004 | --- |
| 損耗因數(shù) | 1.6mm(0.063in),23℃(73?H) | ASTM D-2520 B | 0.004 | --- |
| 損耗因數(shù) | 3.2mm(0.125in),23℃(73?H) | ASTM D-2520 B | 0.004 | --- |
| 介電常數(shù) | 3.2mm(0.125in),23℃(73?H) | ASTM D-150 | 3.9 | --- |
| 介電常數(shù) | 0.8mm(0.032in),23℃(73?H) | ASTM D-2520 B | 4.4 | --- |
| 介電常數(shù) | 1.6mm(0.063in),23℃(73?H) | ASTM D-2520 B | 4.3 | --- |
| 介電常數(shù) | 3.2mm(0.125in),23℃(73?H) | ASTM D-2520 B | 4.3 | --- |
| 損耗因數(shù) | 1×102Hz | IEC 60250 | 150 | --- |
| 損耗因數(shù) | 0.8mm(0.032in),23℃(73?H) | ASTM D-150 | 0.013 | --- |
| 損耗因數(shù) | 3.2mm(0.125in),23℃(73?H) | ASTM D-150 | 0.013 | --- |
| 損耗因數(shù) | 0.8mm(0.032in),23℃(73?H) | ASTM D-150 | 0.026 | --- |
| 熱 性 能 | 解鏈溫度范圍 | --- | --- | 350-360 | ℃ |
| 模壓溫度范圍 | --- | --- | 90 | ℃ |
| 干燥溫度 | --- | --- | 130 | ℃ |
| 熔體溫度 | --- | ISO 3146-C | 335 | ℃ |
| 其它性能 | 工業(yè)含水量 | --- | --- | <0.01 | % |
產(chǎn)品關(guān)鍵詞：
LCP液晶聚酯,美國杜邦,5130L,
![供應(yīng)液晶聚酯LCP 美國杜邦 5130L 玻釬增強]()