| 與典型值比較查找替代品添加到“我的材料” PDF 數(shù)據(jù)表電子郵件打印聯(lián)系 UL IDES |
所有數(shù)據(jù)一般信息物理性能力學(xué)性能熱性能其它加工信息 | 單位英制|公制 |
產(chǎn)品說(shuō)明 | ||||||||
DuPont? Nucrel? 2806 is a tough, lightweight, easily processed ethylene acid copolymer resin, made from nominally 18 wt% acrylic acid. This resin is inherently flexible without the need for plasticizers. The resin can be pigmented, UV-stabilized for exterior applications and painted or plated for special decorative effects. | ||||||||
總體 | ||||||||
材料狀態(tài) | ·已商用：當(dāng)前有效 | |||||||
資料 1 | ·Technical Datasheet (English) | |||||||
搜索 UL 黃卡 | ·DuPont Packaging & Industrial Polymers | |||||||
供貨地區(qū) |
| |||||||
性能特點(diǎn) | ·良好粘結(jié)性 | |||||||
用途 |
| |||||||
機(jī)構(gòu)評(píng)級(jí) | ·FDA 21 CFR 177.1310 (a) 2 | |||||||
形式 | ·顆粒料 | |||||||
物理性能 | 額定值 | 單位制 | 測(cè)試方法 | |||||
比重 | 0.940 | g/cm3 | ASTM D792, ISO 1183 | |||||
熔流率 (190°C/2.16 kg) | 60 | g/10 min | ASTM D1238, ISO 1133 | |||||
硬度 | 額定值 | 單位制 | 測(cè)試方法 | |||||
硬度計(jì)硬度 (邵氏 D) | 52 | ASTM D2240, ISO 868 | ||||||
機(jī)械性能 | 額定值 | 單位制 | 測(cè)試方法 |
抗張強(qiáng)度 | |||
斷裂, 模壓成型 2 | 22.6 | MPa | ASTM D638 |
斷裂, 模壓成型 | 22.6 | MPa | ISO 527-2/51 |
伸長(zhǎng)率 | |||
斷裂, 模壓成型 2 | 460 | % | ASTM D638 |
斷裂, 模壓成型 | 460 | % | ISO 527-2/51 |
彎曲模量 | 38.6 | MPa | ASTM D790 |
沖擊性能 | 額定值 | 單位制 | 測(cè)試方法 |
拉伸沖擊強(qiáng)度 (23°C) | 372 | kJ/m2 | ASTM D1822 |
熱性能 | 額定值 | 單位制 | 測(cè)試方法 |
維卡軟化溫度 | 48.0 | °C | ASTM D1525, ISO 306 |
熔融溫度 | 83.0 | °C | DSC, ISO 3146 |
補(bǔ)充信息 | |||
Acrylic Acid Content: 18% | |||
擠出 | 額定值 | 單位制 | |
第1氣缸區(qū)溫度 | 160 | °C | |
第2氣缸區(qū)溫度 | 182 | °C | |
第3氣缸區(qū)溫度 | 193 | °C | |
第4氣缸區(qū)溫度 | 204 | °C | |
第5氣缸區(qū)溫度 | 204 | °C | |
熔體溫度 | 149 到 232 | °C | |
模具溫度 | 204 | °C | |