PMMA IR-D70 三菱麗陽株式會(huì)社 物性數(shù)據(jù) |
②原料技術(shù)數(shù)據(jù)
| 性能項(xiàng)目 |
試驗(yàn)條件[狀態(tài)] |
測(cè)試方法 |
測(cè)試數(shù)據(jù) |
數(shù)據(jù)單位 |
| 基本性能 |
吸水率 |
24hr |
ASTM D-570 |
0.4 |
% |
| 熔體流動(dòng)速率 |
230°C.3.8kg |
ASTM D-1238 |
1.3 |
g/10min |
| 物理性能 |
折射率 |
--- |
ASTM D-542 |
1.49 |
nd |
| 比重 |
--- |
ASTM D-792 |
1.14 |
--- |
| 全光線透射系數(shù) |
3.2mm |
ASTM D-1003 |
92 |
% |
| 機(jī)械性能 |
成形收縮率 |
--- |
ASTM D-955 |
0.4-0.8 |
% |
| 抗拉強(qiáng)度 |
ASTM NO.1 |
ASTM D-638 |
300 |
Kg/cm2 |
| 延展率 |
ASTM NO.1 |
ASTM D-638 |
90 |
% |
| 抗彎強(qiáng)度 |
1/4"棒 |
ASTM D-790 |
400 |
Kg/cm2 |
| 彎曲彈性模量 |
1/4"棒 |
ASTM D-790 |
1.3×104 |
Kg/cm2 |
| 懸臂梁式?jīng)_擊強(qiáng)度 |
1/4"付 |
ASTM D-256 |
7 |
kg.cm/cm |
| 洛氏硬度 |
M scale |
ASTM D-785 |
32 |
--- |
| 電氣性能 |
表面電阻系數(shù) |
--- |
JIS K-6911 |
>1016 |
Ω |
| 體積電阻系數(shù) |
--- |
JIS K-6911 |
>1015 |
Ω.m |
| 絕緣擊穿強(qiáng)度 |
--- |
JIS K-6911 |
15 |
kv/mm |
| 介電常數(shù) |
60HZ |
JIS K-6911 |
3.9 |
--- |
| 介質(zhì)損耗角正切 |
60HZ |
JIS K-6911 |
0.04 |
--- |
| 耐電弧性 |
--- |
JIS K-6911 |
沒有痕跡 |
--- |
| 熱 性 能 |
維卡軟化溫度 |
1kg |
ASTM D-1525 |
95 |
°C |
| 比熱 |
--- |
--- |
0.35 |
cal/g/°C |
| 線膨脹系數(shù) |
--- |
ASTM D-696 |
11.5×10-5 |
cm/cm/°C |
| 熱傳導(dǎo)系數(shù) |
--- |
ASTM D-177 |
5×10-4 |
cal/s/cm/°C |
| 載荷撓曲溫度 |
18.56kg/cm2 |
ASTM D-648 |
80 |
°C |
|
|
|
|
|
|
|
|