GPPS超高接枝率17% 馬來酸酐接枝PS 巴斯夫 PS-35 透明級ABS共混增韌相容劑 產(chǎn)品說明：
馬來酸酐接枝PS(PS-35)產(chǎn)品說明
The Introduction Of MAH-PS(PS-35)
特 性： 本品為馬來酸酐接枝的PS共混物，外觀：淡黃色顆粒，接枝率：15-18%，熔融指數(shù)：(200℃，5Kg)：1.0-3.0g/10min。該產(chǎn)品具有接枝率高，接枝完全，無毒、無味的特點，克服了馬來酸酐接枝物濃烈的氣味。
Property: The product is the mixture that MAH was grafted onto PS. Appearance: light yellow particle; Grafting ratio: 15-18%; MFR(200℃,5Kg):1.0-3.0g/10min. The product is of high grafting ratio, grafting thoroughly, no poison, no smell. Overcoming the strong thick which made by MAH was grafted onto the resin..
用 途：
1．可作為玻纖增強ABS、AS、礦物填充ABS界面改性劑。馬來酸酐接枝PS賦予了ABS極性，只要添加少量的馬來酸酐接枝PS就可以大幅度提高ABS、AS與玻纖的結合力，使增強ABS、增強AS的拉伸強度、彎曲強度等明顯提高。
2．可作為尼龍與ABS，PC與ABS共混合金的相容劑。
Usage:
1.Used as interface modifier in glass-fiber strengthening ABS, AS and filling ABS. ABS can be given polarity if MAH was grafted onto it. Adding a little PS-35 can improve widely the adhesive between ABS and AS, strengthen ABS, tensile strength and tension strength of AS and so on.
2. Used as compatibilizer in blending alloy of nylon and ABS, PC and ABS .
表一（Figure 1）：ABS樹脂玻纖增強典型數(shù)據(jù)（Typical data of ABS/GF）
性能（Performance） | 單位（Unit） | ABS+GF30% | ABS+GF30%+3%(PS-35) |
拉伸強度（Tensile strength） | MPa | 70 | 120 |
彎曲強度（Flexural strength） | MPa | 100 | 143 |
懸臂梁沖擊強度 | KJ/m2 | 4 | 10 |
表二（Figure 2）：PA6/ABS合金典型數(shù)據(jù)（Typical data of PA6/ABS alloy）
性能（Performance） | 單位（Unit） | PA6+ABS20% | PA6+ABS15%+5%(PS-35) |
拉伸強度（Tensile strength） | MPa | 46 | 51 |
彎曲強度（Flexural strength） | MPa | 65 | 72 |
懸臂梁沖擊強度 | KJ/m2 | 6 | 9 |
注：上述數(shù)據(jù)為實驗典型值，真實可靠。僅供參考，不作為正式質保承諾。
Notice: Above data is experiment typical, true and reliable .It isn’t commitment of the quantity guarantee, but reference
使用方法：按比例與ABS、PC、PA等樹脂混合造粒。
包裝及儲運：25Kg牛皮紙袋內襯塑料袋裝，按非危險品，在干燥條件下儲運，避日光、雨淋。
Packing, storage and transportation:Packed in 25Kg cow parchment takes with plastic takes inside. Not dangerous goods. Store and transport it at dry circumstance. Avoid sunlight and rain.