產(chǎn)品關(guān)鍵詞:
尼龍PA66,押出級管材,PA66原料顆粒,
尼龍PA66押出級管材/PA66原料顆粒
| PA66 42A 美國杜邦公司 物性數(shù)據(jù) |
①原料描述部分規(guī)格級別: | --- | 外觀顏色: | --- |
用途概述: | 應(yīng)用于汽車排檔,機(jī)用存儲原料 |
備注說明: | 特點:有色,高粘綢性,分子量分布密,可焊接于超聲波。 |
②原料技術(shù)數(shù)據(jù)性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 |
物理性能 | | | | | |
吸水率 | immersion 24h;DAM | ASTM D570 | 1.2 | % |
吸水均衡性 | 50% RHL;DAM | Similar to ISO 62 | 2.6 | % |
| | ASTM D570 | Similar to ISO 62 |
| | |
粘性系數(shù)測試 | Viscosity Number;DAM | ISO 307 | 275 | cm3/g |
| Parallel;2.0mm;DAM | Flow;3.2mm(0.126in);DAM |
| | | |
線型模量收縮率橫向 | 2.0mm;DAM | ISO 294-4 | 0.014 | cm/cm |
機(jī)械性能 | | | | | |
| | | | |
| | | | |
| | ASTM D638 | ISO 527 | ASTM D638 |
| | |
| | | | |
| | ISO 178 | ASTM D790 | ISO 178 | ASTM D790 |
| | |
| | | | |
| | | | |
| | | | |
| | | | |
| | | | |
| | | | |
| | | | |
| | | | |
拉力抗沖強(qiáng)度 | Long specimen;DAM | ASTM D1822 | 535 | KJ/m2 |
| | | | |
電氣性能 | | | | | |
| 100Hz;50%RH | DAM | MHz;DAM | DAM | DAM |
| IEC 60250 | ASTM D150 | IEC 60250 | ASTM D150 | ASTM D150 |
| | |
| 1MHz;50%RH | 100Hz;DAM | 50%RH | 50%RH | 50%RH |
| IEC 60250 | IEC 60250 | ASTM D150 | ASTM D150 | ASTM D150 |
| | |
| 100Hz;DAM | 100Hz;DAM | 1KHz;DAM | 1MHz;DAM |
| ASTM D150 | IEC 60250 | ASTM D150 | ASTM D150 |
| | |
加工性能 | 熔融溫度 | DAM | --- | 280-300 | ℃ |
模量溫度 | DAM | --- | 50-90 | ℃ |
干燥損失率 | DAM | --- | Max0.05 | % |
熱 性 能 | 氧氣指數(shù) | DAM | ISO 4589-1/-2 | 28 | % |
| | | | |
| | | | |
| | | | |
| 1.5mm;DAM | 1.5mm;DAM | 0.71mm;DAM | 0.71mm;DAM | 3.0mm;DAM | 3.0mm;DAM |
| UL 94 | IEC 60695-11-10 | IEC 60695-11-10 | UL 94 | IEC 60695-11-10 | UL 94 |
| | |
| Parallel;23-55℃(73-130°F);DAM | Parallel;23-55℃(73-130°F);DAM |
| | | |
熱膨脹系數(shù) | 線型20℃下橫流 | 線型20℃下橫流 |
| 23-55℃(73-130°F);DAM | 23-55℃(73-130°F);DAM |
| | | |
| | | | |
| at 0.46 MPa | at 0.46 MPa | at 1.8 MPa | at 1.8 MPa |
| ISO 75-1/-2 | ASTM D648 | ASTM D648 | ISO 75-1/-2 |
| | |
脆化溫度 | DAM | ASTM D746 | -100 | ℃ |
其它性能 | 顏色 | --- | --- | 天然 | --- |
形式 | --- | --- | 粒子 | --- |
| | | | |